Performance Characteristic
Mixed soap thickening technology, with excellent water resistance.
Excellent lubrication performance, high and low temperature performance and long life.
Excellent anti-rust performance, effectively prevent the corrosion of mechanical parts.
Excellent mechanical stability, to ensure that the grease will not be soft loss.
Recommended Application
Suitable for lubrication of wheel bearings, chassis, pumps, generators and other mechanical equipment of automobiles.
Operating temperature: -20°C ~160℃.
Typical Data
| Item | Typical data | Test method | ||
| NLGI 1 | NLGI 2 | NLGI 3 | ||
| Appearance | Smoothing cream | Visual | ||
| Worked cone penetration, 0.1mm | 315 | 270 | 228 | GB/T 269 |
| Dropping point, ℃ | 257 | 264 | 270 | GB/T 3498 |
| Penetration change after 100,000 strokes, 0.1mm | 9 | 10 | 11 | GB/T 269 |
| Carrying capacity (four ball method) PB value, N | 696 | 696 | 696 | SH/T 0202 |
| Carrying capacity (four ball method) PD value,N | 2450 | 2450 | 2450 | SH/T 0202 |
| Carrying capacity (Timken method) OK value,N | 156 | 156 | 156 | SH/T 0203 |
| Anti-corrosion property(52℃,48h) | Up to standard | GB/T 5018 | ||
| Steel mesh oil separation(100℃，24H)% | 1 | 0.5 | 0.4 | SH/T 0324 |
| Similar viscosity (-10°C,10s-1),Pa·s | 378 | 680 | 986 | SH/T 0048 |
Performance Characteristic
Mixed soap thickening technology, with excellent water resistance.
Excellent lubrication performance, high and low temperature performance and long life.
Excellent anti-rust performance, effectively prevent the corrosion of mechanical parts.
Excellent mechanical stability, to ensure that the grease will not be soft loss.
Recommended Application
Suitable for lubrication of wheel bearings, chassis, pumps, generators and other mechanical equipment of automobiles.
Operating temperature: -20°C ~160℃.
Typical Data
| Item | Typical data | Test method | ||
| NLGI 1 | NLGI 2 | NLGI 3 | ||
| Appearance | Smoothing cream | Visual | ||
| Worked cone penetration, 0.1mm | 315 | 270 | 228 | GB/T 269 |
| Dropping point, ℃ | 257 | 264 | 270 | GB/T 3498 |
| Penetration change after 100,000 strokes, 0.1mm | 9 | 10 | 11 | GB/T 269 |
| Carrying capacity (four ball method) PB value, N | 696 | 696 | 696 | SH/T 0202 |
| Carrying capacity (four ball method) PD value,N | 2450 | 2450 | 2450 | SH/T 0202 |
| Carrying capacity (Timken method) OK value,N | 156 | 156 | 156 | SH/T 0203 |
| Anti-corrosion property(52℃,48h) | Up to standard | GB/T 5018 | ||
| Steel mesh oil separation(100℃，24H)% | 1 | 0.5 | 0.4 | SH/T 0324 |
| Similar viscosity (-10°C,10s-1),Pa·s | 378 | 680 | 986 | SH/T 0048 |